FORTECOAT Laser Cladding Powders
FORTECOAT Laser Cladding Powders
Laser Cladding is a method of depositing material by which a powdered material is melted and consolidated by use of a focused laser beam in order to coat part of a substrate.
Process Advantages
- Powdered material can be placed precisely where desired
- Very good metallurgically bonded and fully dense coatings with little or no porosity
- Minimal heat affected zone and low dilution
- Excellent process stability and reproducibility because it is easy to automate and integrate into CNC production
- Limited distortion due to minimal heat input
Nickel Based Powders
| Product Code | Hardness | Alloy Composition |
|---|---|---|
| 9062 | 57-62 HRC | Ni Cr15.5 B2.9 Si4.3 C0.7 Fe4.2 |
| 9056 | 52-58 HRC | Ni Cr13.5 B2.8 Si4 C0.55 Fe3.9 |
| 9053 | 47-53 HRC | Ni Cr12.5 B2.3 Si3.3 C0.5 Fe3.9 |
| 9033 | 30-35 HRC | Ni Cr8 B1.5 Si3.6 C0.32 Fe2.6 |
| 9045 | 36-40 HRC | Ni Cr10.3 B2 Si3.2 C0.38 Fe2.4 |
| 9238 | 36-40 HRC | Ni B2.1 Si3 |
| 9249 | 48-52 HRC | Ni B3 Si3 |
| 9265 | Ni Cr21.5 Fe0.35 Mo9 Nb3.5 Mn0.5 (Inconel 625) |
Cobalt Based
| Product Code | Hardness | Alloy Composition |
|---|---|---|
| 42001 | 53-58 HRC | Co Cr30 C2.5 W12 Mo<1 Ni<2 Si Fe Mn |
| 42006 | 40-44 HRC | Co Cr28.5 C1.1 W4.4 Mo<1 Ni<2 Si Fe Mn |
| 42006H | 40-46 HRC | Co Cr29 C1.2 W5.2 Mo<1 Ni<2 Si Fe Mn |
| 42012 | 47-51 HRC | Co Cr28.5 C1.4 W8 Mo<1 Ni<2 Si Fe Mn |
| 42021 | 28-40 HRC | Co Cr27 C0.25 Mo5.5 Ni2.6 Si Fe Mn |
| 42000F | 42-46 HRC | Co Cr26 C1.75 W12 Mo<1 Ni22.5 Si Fe Mn |
Iron Based
| Product Code | Hardness | Alloy Composition |
|---|---|---|
| 304L | <200 HV | Fe Cr18 C<0.04 Si0.5 Ni11 Mn1.3 |
| 316L | <200 HV | Fe Cr17 C0.02 Si0.8 Ni13 Mn1.5 Mo2.2 |
| 410 | * | Fe Cr12.5 C0.12 Si0.3 |
| 420 | * | Fe Cr13 C0.2 Si0.5 Mn0.5 |
*Hardness values are according to heat treatment.
*Other alloy compositions are available.
WC-Ni Alloy Matrix Powder for Laser Cladding
| Product Code | Nickel Matrix | WC |
|---|---|---|
| 15750 | 55 HRC powder 50% | WC-spherical 50% |
| 15760 | 55 HRC powder 40% | WC-spherical 60% |
*Other or customer specific blends are available.
- Partical size
44 – 125 µm
53 – 150 µm
63 – 210 µm
equipment specific - Applications
Most common uses of PTA in glass industry are moulds, bottom-plates and guide-rings.
- Documents
ForteCoat thermal spray powders for glass moulds industry brochure 
ForteCoat thermal spray powders general brochure